Mixing Steps:
Loading of about 80% is expected to be mixed into the batch size of the water, and with the mixer running, slowly add the required amount of cement. Allow sufficient time for the slurry mix to a creamy consistency, add before pumping or filler material (sand, fly ash, etc.) was slowly added sand, if necessary, until just blended cement began to lose color. This should be the maximum number of mixed sand can hold, it may be necessary to use a little less sand for subsequent batches. Water can be used for relative humidity or dry sand to produce a slurry, which is just pourable adjusted.
Premix Filling:
Many suppliers of building materials manufacture of Portland cement-based mortar premix, some of which are pumpable, and some are non-pumpable. Before attempting pumping premixed grout material, determine whether the material meets the above criteria. It is also necessary to determine whether the material is set before, because there may be insufficient time to work pumping shorter working hours. Gaode have tested many major manufacturers grouting products. Before pumping any premixed cement-based mortar composition, it was mentioned earlier before pumping grout pump and mixing lines with mixed cement and water slurry, is good practice to first coat.
Homemade Grout
Commercially prepared slurry is sometimes difficult to obtain, but in these cases, it may be necessary to develop and materials production site. This can be done very successfully, but some basic principles must be observed.
The resulting material should exhibit the following characteristics:
1. Stable suspension, which is not separated from the rest of the solid.
2. It must be the main color of the cement used.
3. Enough liquid poured from the container, but not too wet. (Thick batter consistency)
Cement
There are several types of Portland cement manufactured to meet specific requirements, such as high early strength, sulfate resistance, and other needs. The most common are Type I Portland, and is the most often used in the production of cement grout.
Water
In most cases, water is used to produce water slurry should be clean and free sulfate or other chemicals dissolved. If drinking water is ideal. Since the ratio of water to cement is the most important factor in the quality of its final state of the material, the water content should be kept to the minimum requirement will be generated and the properties of the materials listed above.
Admixtures
Admixtures can be used to modify and enhance the grout mixture. These include plasticizers, water reducing agents, bulking agents, anti-erosion and other ingredients. If used at all, they should only they fully understand the effect of the use, and only in accordance with manufacturer recommendations.
Flyash
In some parts of the country, flyash (a byproduct of coal-fired power plants) is available. This material is often used to enhance or reduce the performance of the cement slurry, in some cases, the cement fraction. The use of such material should be treated with caution, because some sources of ash has been observed to result in flash setting grout mix. If you use the product for a trial mix should demonstrate its applicability.
Sand
If you use sand sand expected, there are several factors must be considered such as shape, size and gray sand is used. Under normal circumstances, the sand should be clean, well graded rounded and natural shape. Should avoid angular particles, such as sand manufacturing. A greater number of holes and circular gradient mixing ratio of sand particles in the sand its poor ratings, or has a flat, a significant number of sharp or angular particles are used. Concrete sand usually not pumpable, but masonry and plaster sand is usually pumpable.